Title: Aging of Cast 35Cr–45Ni Heat Resistant Alloys With Different Carbon Content
Authors: 64490
Issue Date: 22-Dec-2016
Publisher: ASTM Internacional
Abstract: Lo cambios microestructurales que toman lugar dos aleaciones resistentes al calor después del envajecimiento a 750 ºC por un periodo de tiempo de 1000 h se reporta en este trabajo. Las aleaciones seleccionadas tienen un composición similar, con excepción del contenido de carbono que fue de 0.15 y 0.50 %. Los materiales fueron obtenidos de tubos vaciados centrifugamente y su microestructura fuenhecha de una matriz austenítica dentrítica y carburos interdentríticos primarios, fueron analizadas con microscopía electrónica de barrido y óptica lo que condujo a identificar los carburos como NbC y Cr7C3. Analizando áreas específicas se cuantificaron los carburos primarios en su condición de material nuevo y envejecido; estos análisis revelaron que su cantidad no se afectó con el envejecimiento, pero dependiendo del contenido de su carbono, con la predominancia de NbC en la aleación con menor contenido de carbon, debido a su alta afinidad del carbono para el niobio. El envejecimiento afectó las partículas NbC, transformándolas en silicatos, se dió precipitación de carburos secundarios Cr23C6, mientras Cr7C3 permaneció sin cambios. Los cambios microestructurales que fueron observados por micoscopía fueron confirmados por difracción de rayos X. Las propiedades mecánicas de los materiales como dureza y resistencia a la tensión se incrementaron, mientras la ductilidad en ambas aleaciones se redujo.
Description: The changes in microstructure that took place in two heat-resistant after aging alloys at 750􏰀 C for a period of time of up to 1000 h are reported in this work. The alloys selected had a similar composition, with the exception in carbon content that was of 0.15 and 0.50 %. The material was obtained from centrifugal cast pipes and their microstructure was made of an austenitic dendrite matrix with interdendritic primary cabides; light optical and scanning electron microscopy analyses were conducted to identify these carbides as NbC and Cr7C3. Selected area analyses were conducted to quantify the primary carbides in the as-cast and aged conditions; these analyses revealed that their amount was unaffected by aging, but depended on the carbon content, with the predominance of NbC in the alloy with lower carbon content, due to the higher affinity of carbon to niobium. Aging affected the NbC particles, as they transformed into silicides, precipitation of secondary Cr23C6 particles took place, while Cr7C3 remained unaffected. The changes in microstructure that were observed by microscopy were confirmed by X-ray diffraction. The mechanical properties of the materials changed, as hardness and tensile strength increased, while the ductility in both alloys was reduced.
URI: http://ricaxcan.uaz.edu.mx/jspui/handle/20.500.11845/1751
ISSN: 2379-1365
2165-3992
Other Identifiers: info:eu-repo/semantics/publishedVersion
Appears in Collections:*Documentos Académicos*-- M. en Ciencias de la Ing.

Files in This Item:
File Description SizeFormat 
MPC_v5_2016_p675.pdfArtículo, Materials Performance Chacacterization, 201635,97 kBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons