Guayaquil Sosa, Jesús Fabricio; Serrano Rosales, Benito; Valadés Pelayo, Patricio Javier; de Lasa, Hugo
Resumen:
A series of mesoporous TiO2 (meso-TiO2) were synthesized using the sol-gel technique. A Pluronic F127
triblock-copolymer, a structure-directing agent, was incorporated as a soft template into the sol-gel. In
addition, and during a separate synthesis, the sol-gel was doped with a Pt precursor. Semiconductors
were prepared with 1.00 wt.%, 2.50 wt.%, 5.00 wt.% Pt nominal loadings, respectively. They were calcined
at 500 ◦C and 550 ◦C following synthesis. Morphological and structural properties were studied by: a)
X-ray diffraction, b) UV–vis spectrophotometry, c) N2 adsorption-desorption (BET, BJH), and d) X-ray
photoelectron spectroscopy (XPS). Optical band gap values for meso-TiO2 and Pt-meso-TiO2 were cal-
culated by Kubelka-Munk (K-M) function coupled with Tauc plot methodology. It was observed that the
prepared semiconductors displayed pore sizes in the 10–40 nm range with bimodal distributions. Their
photocatalytic activity forhydrogenproductionvia water splitting was established ina Photo-CRECWater-
II reactor under near-UV light irradiation. The aqueous solution contained 2% v/v ethanol, employed as
a renewable organic scavenger. The prepared semiconductors showed that the mesoporous 2.50 wt.%
Pt-TiO2 has the highest photoactivity for hydrogen generation. This suggests the important role played
by the loading of platinum as a TiO2 dopant, reducing the optical band gap, increasing electron storage
and diminishing, as a result, electron-hole recombination. The measured Quantum Yield (QY), obtained
using a rigorous approach, was established for the mesoporous 2.50 wt.% Pt-TiO2 at a promising level of
22.6%.