Esparza Salazar, Diego; Sidhik, Siraj; López Luke, Tzarara; Rivas Martínez, Jesús Manuel; De la Rosa, Elder
Resumen:
CsPbBr3 perovskite nanocrystals (PNCs) have been synthesized using the hot injection method. The CsPbBr3 PNCs exhibit a high photoluminescence quantum yield (PLQY) of 73%. A comprehensive study of UV light interaction with the CsPbBr3 PNCs was performed. SEM images, photolumines- cence spectra, x-ray Diffraction and PLQY measurements were obtained for different time of UV exposure. The exposure to UV light modifies the crystal size (from 10 ×10 nm to 12 × 95 nm) and morphology (change from nanocubic to nanorods form). The XRD spectra show a change from tetragonal to cubic crystalline structure. In addition, the interaction of UV light modifies the optical properties of the PNCs by varying the photoluminescence. The material remains stable for a period of 1 h, however, with exposure to UV light, the PNCs show a decrement in QY from 73.3% to 46.6% after 30 days. These results indicate that light-induce variation in morphological and photo-stability of CsPbBr3 PNCs.